Deposition of N-doped poly-Si films from SiH4 and NH3 using a single wafer type low pressure chemical vapor deposition (LPCVD) system was investigated to improve the grain size reduction and the grain size distribution. The deposition rate and surface roughness of N-doped Si were greatly affected by the NH3/SiH4 ratio such that they decreased with increasing NH3/SiH4 ratio. X-ray diffraction (XRD) and transmission electron microscopy (TEM) measurements revealed that with increasing NH3/SiH4 ratio, the size of the grains was decreased and the grains size distribution became uniform. Finally, we successfully obtained N-doped poly-Si films having uniform grain size of approximately 6 nm.
Mori S, Yamaguchi Y, Sato M, Meguro H, Tsunda H, Kamiya E, Yoshikawa K, Arai N, Sakagami E, IEEE Trans. Electron Devices, 43, 47, 1996
Nkansah FD, Hatalis M, IEEE Trans. Electron Devices, 46, 1355, 1999
Muramatsu S, Kubota T, Nishio N, Shirai H, Matsuo M, Kodama N, Horikawa M, Saito S, Arai K, Okazawa T, IEDM Tech. Dig., 847, 1994
Togo M, Suzuki T, Hasegawa E, Koyama S, Fukai T, Sakakidani A, Miyake S, Watanabe T, Yamamoto I, Tanaka M, Kawashima Y, Kunimune Y, Ikeda M, Imai K, 2006 Symp. VLSI Tech. Dig. Technical Papers, 30, 2006