Characteristics of Li2CO3 as sintering aid for Ce0.8Sm0.2 O2-δ electrolyte in solid oxide fuel cells
Owing to its excellent ionic conductivity, 20 mol% samarium doped ceria (Ce0.8Sm0.2O2-δ, SDC) is considered a promising alternative as an electrolyte in solid oxide fuel cells (SOFCs). SDC electrolytes, however, require high sintering temperatures over 1,600 ℃ to attain sufficient density to be SOFC electrolytes. To lower the SDC sintering temperature, different amounts of Li2CO3 (0-12mol% of Li) were evaluated as a sintering aid for SDC electrolytes. The SDC electrolyte samples with Li were sintered at 1,400 ℃ and were compared with SDC electrolytes sintered at 1,600 ℃. The SDC electrolyte with 6mol% of Li sintered at 1,400 ℃ (Li6SDC1400) was densified to 97.495% of theoretical density (T.D.), which is similar to that achieved by the SDC electrolyte sintered at 1,600 ℃ (97.433% of T.D.). The improved formation of grain boundary in the Li6SDC1400 sample increased the density of the SDC, resulting in enhancement of ionic conductivity and cell performance. At 800 ℃, the maximum power density of the Li6SDC1400 electrolyte sample was 120.15mW/cm2.
[References]
- Lee JM, Yun JW, Ceram. Int., 42, 8698, 2016
- Zhan Z, Lin Y, Pillai M, Kim I, Barnett SA, J. Power Sources, 161, 460, 2006
- Ormerod RM, Chem. Soc. Rev., 32, 17, 2003
- Brett DJ, Alan A, Brandon NP, Skinner SJ, Chem. Soc. Rev., 37, 1568, 2008
- Jo DH, Chun JH, Park KT, Hwang JW, Lee JY, Jung HW, Kim SH, Korean J. Chem. Eng., 28, 1844, 2011
- Kim JH, Park YM, Kim T, Kim H, Korean J. Chem. Eng., 29, 349, 2012
- Chen M, Zhang H, Fan L, Wang C, Zhu B, Int. J. Hydrog. Energy, 39, 12309, 2014
- Zinkevich M, Djurovic D, Aldinger F, Solid State Ion., 177, 989, 2006
- Zhu T, Lin Y, Yang Z, Su D, Ma S, Han M, Chen F, J. Power Sources, 261, 255, 2014
- Wang X, Ma Y, Raza R, Muhammed M, Zhu B, Electrochem. Commun., 10, 1617, 2008
- Singh B, Bhardwaj A, Gautam SK, Kumar D, Parkash O, Kim IH, Song SJ, J. Power Sources, 345, 176, 2017
- Zhang G, Li W, Huang W, Cao Z, Shao K, Li F, Tang C, Li C, He C, Zhang Q, Fan L, J. Power Sources, 386, 56, 2018
- Khan I, Tiwari PK, Basu S, Electrochim. Acta, 294, 1, 2019
- Zhang X, Deces-Petit C, Yick S, Robertson M, Kesler O, Maric R, Ghosh D, J. Power Sources, 162, 480, 2006
- Fan L, Wang C, Chen M, Zhu B, J. Power Sources, 234, 154, 2013
- Zhu B, Li S, Mellander BE, Electrochem. Commun., 10, 302, 2008
- Chen PL, Chen IW, J. Am. Ceram. Soc., 79, 3129, 1996
- Chen PL, Chen IW, J. Am. Ceram. Soc., 80, 637, 1997
- Tianshu Z, Hing P, Huang H, Kilner J, J. Mater. Process. Technol., 113, 463, 2001
- Herring C, J. Appl. Phys., 21, 301, 1950
- Wang J, Chen X, Xie S, Chen L, Wang Y, Meng J, Zhou D, J. Power Sources, 428, 105, 2019
- Le S, Zhu S, Zhu X, Sun K, J. Power Sources, 222, 367, 2013
- Yoshida H, Inagaki T, J. Alloy. Compd., 408, 632, 2006
- Villas-Boas LA, Figueiredo FMI, de Souza DPF, Marques FBM, Solid State Ion., 262, 522, 2014
- Wei T, Jia L, Luo J, Chi B, Pu J, Li J, Appl. Surf. Sci., 506, 144699, 2020
- Guo X, Solid State Ion., 81, 235, 1995
- Guo X, Solid State Ion., 96, 247, 1997
- Guo X, Comput. Mater. Sci., 20, 168, 2001
- Guo X, Sigle W, Fleig J, Maier J, Solid State Ion., 154, 555, 2002
- Guo X, Zhang Z, Acta Mater., 51, 2539, 2003
- M’Peko JC, de Souza MF, Appl. Phys. Lett., 83, 737, 2003
- Guo X, Waser R, Prog. Mater. Sci., 51, 151, 2006
- Ruifeng G, Zongqiang M, J. Rare Earth, 25, 364, 2007
- Prakash BS, Kumar SS, Aruna SR, B. Mater. Sci., 40, 441, 2017
- Nie X, Chen Y, Mushtaq N, Rauf S, Wang B, Dong W, Wang X, Wang H, Zhu B, Nanoscale Res. Lett., 14, 1, 2019
|