This is an Open-Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/bync/3.0) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.

All issues

Enhanced Performance of Proton Exchange Membrane Fuel Cells Using Platinum–Iron Oxide Catalysts Supported on Activated Carbon Spheres

Arzu Ekinci Abdurrahman Akdag¹ Kaan Büyükkanber² Ömer Şahin^2†

Department of Occupational Health and Safety, Faculty of Health Sciences , Siirt University ¹Vocational School of Health Services , Harran University ²Department of Chemical Engineering, Faculty of Chemical and Metallurgical Engineering , Istanbul Technical University

omersahin@itu.edu.tr

Korean Journal of Chemical Engineering, October 2025, 42(12), 2935-2950(16)
https://doi.org/10.1007/s11814-025-00516-y

Abstract

In this study, the electrochemical performance of Fe 3 O 4 -supported Pt/C catalysts was evaluated in a Proton exchange

membrane fuel cell (PEMFC), with a focus on enhancing oxygen reduction reaction (ORR) kinetics. Fe 3 O 4 nanoparticles

reduced catalyst particle sizes and improved structural stability. Among the catalysts tested—Pt-Fe 3 O 4 magnetic nanoparticle

(MNP)/C, Pt/ Fe 3 O 4 MNP-C, and Pt/ Fe 3 O 4 activated carbon sphere (ACS)-C—the Pt/ Fe 3 O 4 MNP-C variant achieved the

highest power density (215 mW/cm 2 at 346 mA/cm 2 ) and displayed superior activity. Analytical techniques such as XRD,

SEM–EDX, and TEM confi rmed the superior crystallinity and phase purity of the Pt/ Fe 3 O 4 -based catalysts. Particle sizes

were found to be 3.16 nm, 2.71 nm, and 4.70 nm, respectively, for Pt-Fe 3 O 4 MNP/C, Pt/ Fe 3 O 4 MNP-C, and Pt/Fe 3 O 4 ACSC.

The high ORR activity of Pt/Fe 3 O 4 MNP-C is attributed to the high surface area and conductivity provided by activated

carbon spheres, alongside enhanced Pt-Fe 3 O 4 interactions. Mass activities were recorded at 2829, 2307, and 1893 mA/mg Pt ,

with Pt-Fe 3 O 4 MNP/C showing the fastest kinetics and highest effi ciency. Pt/ Fe 3 O 4 MNP-C emerges as a promising lowplatinum,

high-effi ciency electrocatalyst for PEMFCs, marking a signifi cant step toward sustainable fuel cell technologies.

Keywords

PEM fuel cells · Fe 3 O 4 nanoparticles · Power density · Activated carbon spheres · Electrocatalytic performance