In this study, the characteristics of amorphous silicon etching for the formation of gate electrodes have been evaluated at the variation of several process parameters. When total flow rates composed of Cl2/HBr/O2 gas mixtures increased, the etch rate of amorphous silicon layer increased, but critical dimension (CD) bias was not notably changed regardless of total flow rate. As the amount of HBr in the mixture gas became larger, amorphous silicon etch rate was reduced by the low reactivity of Br species. In the case of increasing oxygen flow rate, etch selectivity was increased due to the reduction of oxide etch rate, enhancing the stability of silicon gate etching process. However, gate electrodes became more sloped according to the increase of oxygen flow rate. Higher source power induced the increase of amorphous silicon etch rate and CD bias, and higher bias power had a tendency to increase the etch rate of amorphous silicon and oxide.