Extraction and phase transformation of iron in fine-grained complex hematite ore by suspension magnetizing roasting and magnetic separation
Suspension magnetizing roasting-magnetic separation technology was used to extract iron from fine-grained complex hematite ore. The effect of roasting conditions on the magnetizing roasting-magnetic separation process was studied. In summary, a concentrate with TFe grade of 69.96% and Fe recovery of 79.02% could be obtained under conditions of a roasting temperature of 500 oC, roasting time was 12 min, reductant concentration of 30%, and total gas flow of 200mL/min, while TFe grade of final tailings was 5.66%. The phase composition and X-ray photoelectron spectroscopy analysis showed that hematite in the sample was transformed into magnetite during suspension magnetization roasting. After roasting, the proportion of Fe content in the phase of the magnetite increased from 5.91% in roasting feed to 97.96% in the roasting product. Transmission electron microscopy results also confirmed that hematite was transformed into magnetite with spinel structure, and the newly formed magnetite had good crystallinity. Scanning electron microscopy and BET analysis showed that roasting could increase the specific surface area, total pore volume, and porosity of the roasted product, which would strengthen the internal diffusion of CO and CO2 in the particles, to improve the reduction rate of hematite. The loose internal structure of roasted particles led to the decrease of mechanical properties, which was conducive to improving the subsequent grinding efficiency.
[References]
  1. Patra S, Pattanaik A, Rayasam V, Can Metall Q., 58, 28, 2019
  2. Yu JW, Han YX, Li YJ, Gao P, Sun YS, Sep. Sci. Technol., 52, 1768, 2017
  3. Sun YS, Zhang XL, Han YX, Li YJ, Powder Technol., 361, 571, 2020
  4. Komljenovic D, Stojanovic L, Malbasic V, Lukic A, Int. J. Min. Sci. Technol., 30, 737, 2020
  5. Lan ZY, Lai ZN, Zheng YX, Lv JF, Pang J, Ning JL, J. Cent. South Univ., 27, 37, 2020
  6. Yu JW, Han YX, Gao P, Li YJ, Yuan S, Li WB, Physicochem. Probl. Mineral Pro., 54, 668, 2018
  7. Abaka-Wood GB, Zanin M, Addai-Mensah J, Skinner W, Miner. Eng., 142, 105888, 2019
  8. He J, Zhu L, Bu X, Liu C, Luo Z, Yao Y, Chem. Eng. Process., 138, 27, 2019
  9. Lima RMF, Abreu FDVF, J. Mater. Res. Technol-JMRT, 9, 2021, 2020
  10. Wang WW, Li ZY, Miner. Eng., 155, 106453, 2020
  11. Matiolo E, Couto HJB, Lima N, Silva K, de Freitas AS, Miner. Eng., 158, 106608, 2020
  12. Li W, Zhou L, Han Y, Zhu Y, Li Y, Powder Technol., 343, 270, 2019
  13. He JF, Liu CG, Xie JQ, Hong P, Yao YK, Powder Technol., 319, 346, 2017
  14. Yao Y, Bai Q, He J, Zhu L, Zhou K, Zhao Y, Waste Manage., 103, 218, 2020
  15. Gao Z, Chai X, Zhou E, Jia Y, Duan C, Tang L, Int. J. Min. Sci. Technol., 30, 883, 2020
  16. Rath SS, Sahoo H, Dhawan N, Rao DS, Das B, Mishra BK, Sep. Sci. Technol., 49, 1927, 2014
  17. Wu FF, Cao ZF, Wang S, Zhong H, J. Alloy. Compd., 722, 651, 2017
  18. Lu SD, Ju SH, Peng JH, Zhu XP, High Temp. Mater. Process., 34, 147
  19. Xu C, Cheng HW, Li GS, Lu CY, Lu XG, Zou XL, Xu Q, Int. J. Miner. Metall. Mater., 24, 377, 2017
  20. Tang ZD, Gao P, Han YX, Guo W, J. Min. Metall. Sect. B-Metall., 55, 295, 2019
  21. Donskoi E, Collings AF, Poliakov A, Bruckard WJ, Int. J. Miner. Process., 114, 80, 2012
  22. Zhou W, Sun Y, Han Y, Gao P, Li Y, Miner. Eng., 164, 106851, 2021
  23. Qin Y, Han Y, Gao P, Li Y, Yuan S, Miner. Eng., 160, 106662, 2021
  24. Sun YS, Zhu XR, Han YX, Li YJ, Gao P, J. Clean Prod., 261, 121221, 2020
  25. Li Y, Zhang Q, Yuan S, Yin H, Powder Technol., 379, 466, 2021
  26. Gao P, Tang ZD, Han YX, Li EL, Zhang XL, Powder Technol., 343, 255, 2019
  27. Tang ZD, Gao P, Li YJ, Han YX, Li WB, Butt S, Zhang YH, Powder Technol., 361, 591, 2020
  28. Yuan S, Zhang Q, Yin H, Li Y, J. Hazard. Mater., 404, 124067, 2021
  29. Petrus HTBM, Putera ADP, Sugiarto E, Perdana I, Warmada IW, Nurjaman F, Astuti W, Mursito AT, Miner. Eng., 132, 126, 2019
  30. Ponomar VP, Dudchenko NO, Brik AB, Miner. Eng., 122, 277, 2018