활성탄을 환원제로 하는 금 속의 산화-환원에 의한 물로부터 수소 제조를 수행하였다. 이용한 금속은 Co, Ni, Fe, Cu, Cr, Pd, Zn 및 Mn이었으며, 온도에 따른 수소의 생성속도를 알아보기 위해서 미소 펄스 반응기에서 실험을 하였다. 그 결과 Co와 Ni이 좋은 금속임을 알 수 있었고, 600℃에서는 석탄기화의 반응계에서 좋은 촉매로 알려진 Na2CO3보다 더 높은 수소 생성량을 나타냈다.
Hydrogen was produced from water by redox cycle of metals using activated carbon as a reduc-tant. Several metals-Co, Ni, Fe, Cu, Pd, Zn and Mn-were used. In order to test the rate of hydrogen production according to temperature, a micropules reactor was used. As a result, it was found that Co and Ni were the best hydrogen producing metals among the metals tested. At 600℃, Co showed the better hydrogen production rate than Na2CO3 that was known as a good catalyst in coal gasification reaction.
[References]
오오다도끼오, "수소에너지," 현대과학신서, 1974
Gustav PD, Int. J. Hydrog. Energy, 14, 777, 1989
Engels H, Funk JE, Hesselmann K, Knoche KF, Int. J. Hydrog. Energy, 12, 291, 1987
Ohta T, Abe I, Int. J. Hydrog. Energy, 10, 275, 1985
Ohta T, Funk JE, Porter JD, Tilak BV, Int. J. Hydrog. Energy, 10, 571, 1985
Bilgen C, Bilgen E, Int. J. Hydrog. Energy, 9, 197, 1984