Improvement of polymer electrolyte membrane by radiation-induced grafting of styrene onto FEP film with subsequent sulfonation
Poly(tetrafluoroethylene-co-hexafluoropropylene) (FEP) film was homogeneously and highly grafted by styrene monomer under simultaneous irradiation with an electron beam, whereas preirradiation with an electron beam was insufficient to accomplish a high degree of grafting without activation of the styrene monomer. Following its subsequent sulfonation, the styrene-grafted FEP film exhibited considerably higher values of both the IEC and IC and less methanol crossover than the Nafion membrane. The grafting of styrene onto the FEP polymer is thought to be initiated by the abstraction of F atoms from the CF3 groups in the polymeric structure. It was estimated that two sulfonic acid groups can be attached to the benzene ring of one styrene molecule. The profile of sulfur across the FEP film, which is related to the concentration profile of sulfonic acid groups inside the styrene-grafted FEP film, became more and more homogeneous over a period of several hours, due to the step by step diffusion of monomers into the film, eventually showing a high IC value of 0.25 S/cm in the case of the 125 μm thick FEP film, whereas Nafion 117 (125 μm thickness) exhibited an IC value of 0.12 S/cm.
Keywords:
Fuel Cell Membrane; FEP; Styrene; Electron Beam; Grafting; Sulfonation; IEC; IC; Sulfur Profile
[References]
- Savadogo O, J. New Mat. Electrochem. Syst., 1, 47, 1998
- Acres GJK, J. Power Sources, 100(1-2), 60, 2001
- Patri M, Hande VR, Phadnis S, Somaiah B, Roychoudhury S, Deb PC, Polym. Adv. Technol., 15, 270, 2004
- Miyake N, Wainright JS, Savinell RF, J. Electrochem. Soc., 148(8), A898, 2001
- Park HB, Lee YM, J. Korean Ind. Eng. Chem., 13(1), 1, 2002
- Xing PX, Robertson GP, Guiver MD, Mikhailenko SD, Wang KP, Kaliaguine S, J. Membr. Sci., 229(1-2), 95, 2004
- Inzelt G, Pineri M, Schultze JW, Vorotyntsev MA, Electrochim. Acta, 45(15-16), 2403, 2000
- Chen JH, Asano M, Yamaki T, Yoshida M, J. Membr. Sci., 269(1-2), 194, 2006
- Lappan U, Geiβle U, Uhlmann S, Nucl. Instrum. Methods Phys. Res. Sect. B-Beam Interact. Mater. Atoms, 236, 413, 2005
- Schmidt TJ, Simbeck K, Scherer GG, J. Electrochem. Soc., 152(1), A93, 2005
- Gupta B, Buchi FN, Scherer GG, Chapiro A, J. Membr. Sci., 118(2), 231, 1996
- Gupta B, Buchi FN, Scherer GG, J. Polym. Sci. A: Polym. Chem., 32(10), 1931, 1994
- Chen JH, Asano M, Yamaki T, Yoshida M, J. Membr. Sci., 256(1-2), 38, 2005
- Yamaki T, Kobayashi K, Asano M, Kubota H, Yoshida M, Polymer, 45(19), 6569, 2004
- Becker W, Bothe M, Schmidy-Naake G, die Angewandte Makromolekulare Chemie, 273, 57, 1999
- Gupta B, Chapiro A, Eur. Polym. J., 10, 1145, 1989
- Gupta B, Buchi FN, Scherer GG, Chapiro A, Polym. Adv. Technol., 5, 493, 1994
- Gupta B, Scherer GG, Chimia, 48, 127, 1994
- Nasef MM, Saidi H, Nor HM, J. Polym. Sci., 76, 220, 2000
- Liang GZ, Lu TL, Ma XY, Yan HX, Gong ZH, Polym. Int., 52, 1300, 2003
- Guta B, Buchi FN, Scherer GG, Solid State Ion., 61, 213, 1994
- Nasef MM, Saidi H, Nor HM, Foo OM, J. Appl. Polym. Sci., 78(14), 2443, 2000
- Kuver A, Vielstich W, J. Power Sources, 74(2), 211, 1998
- Ravikumar MK, Shukla AK, J. Electrochem. Soc., 143(8), 2601, 1996
- Carrette L, Friedrich KA, Stimming U, Fuel Cells, 1, 5, 2001
- Nasef MM, Zubir NA, Ismail AF, Khayet M, Dahlan KZM, Saidi H, Rohani R, Ngah TIS, Sulaiman NA, J. Membr. Sci., 268(1), 96, 2006
- Meyer G, Perrot C, Gebel G, Gonon L, Morlat S, Gardette JL, Polymer, 47(14), 5003, 2006
참고문헌정보(참고문헌, 인용문헌)는 화학공학소재연구정보센터에 의해 제공되고 있습니다.