Post-sulfonation에 의한 SBS 이온교환막의 제조 및 특성
Preparation and Property of SBS Ion-exchange Membrane Via Post-sulfonation
본 연구에서는 post sulfonation 반응을 통하여 SBS 양이온교환막을 제조하였다. 술폰화 양이온교환막의 술폰화도, 함수율, 이온교환용량, 전기저항 및 전기전도도등 막의 전기적 특성을 술폰화 시간을 변수로 하여 확인하였다. 술폰화 SBS 막의 술폰화도는 반응시간 및 황산의 농도가 증가함에 따라 증가하였으며 최대 술폰화도는 24.0%이었다. 또한 막의 함수율과 이온교환용량은 술폰화도가 증가함에 따라 증가하였으며 각각 41.2%, 0.80 meq/g로 가장 높았으며, 전기저항과 전기전도도는 각각 23.6 Ω·cm2, 4.24×10^(-4) S/cm이었다.
In this study, the sulfonated SBS cation-exchange membrane was prepared by post-sulfonation. Degree of sulfonation(DS), water-uptake, ion exchange capacity and electrical resistance and conductivity of sulfonated SBS were investigated as a function of sulfonation time. The DS of sulfonated SBS membrane was increased with increasing the reaction time and concentration of sulfuric acid. The maximum value of DS was 24.0%. And also, the water uptake and ion exchange capacity of the sulfonated SBS membrane were increased as increasing the value of DS. The values of water uptake and IEC were 41.2% and 0.80 meq/g, respectively. The electrical resistance and conductivity of the membrane showed 23.6 Ω·cm2 and 4.24×10^(-4) S/cm, respectively.
Keywords:
SBS Membrane; Post Sulfonation; Water Uptake; Ion Exchange Capacity; Electrical Resistance
[References]
- Mauhar SM, Barjaktarovic BG, Sovilj MN, Chem. Pap., 58, 386, 2004
- Silva DL, Brunner G, Braz. J. Chem. Eng., 23, 213, 2006
- Singh R, Desalination, 227(1-3), 14, 2008
- Xu TW, J. Membr. Sci., 263(1-2), 1, 2005
- Nagarale RK, Gohil GS, Shahi VK, Adv. Colloid. Inter. Sci., 119, 97, 2006
- Farmer JC, Fix DV, Mack GV, Pekala RW, Poco JF, J. Appl. Electrochem., 26(10), 1007, 1996
- Lee KS, Kim JH, Kim JH, Appl. Chem., 7(1), 129, 2003
- Kariduraganavar MY, Nagarale RK, Kittur AA, Kulkarni SS, Desalination, 197(1-3), 225, 2006
- Yang Y, Holdcroft, Fuel Cells, 2, 171, 2005
- Park HB, Lee YM, J. Korean Ind. Eng. Chem., 13(1), 1, 2002
- Green MA, J. Mater. Sci. - Mater. Electron., 18, 15, 2007
- Baek KW, Cho IH, Nho YC, Hwang TS, Polym.(Korea), 30(6), 525, 2006
- Cho IH, Baek KW, Lim YM, Nho YC, Hwang TS, Polym.(Korea), 31(3), 239, 2007
- Choi KJ, Lee CH, Hwang TS, Polym.(Korea), 32(6), 509, 2008
- Nasef MM, Saidi H, Nor HM, J. Appl. Polym. Sci., 76(2), 220, 2000
- Nasef MM, Saidi H, J. Membr. Sci., 5572, 1, 2003
- Cho IH, Baek K, Lee CS, Nho YC, Yoon SK, Hwang TS, Polym.(Korea), 31(1), 1, 2007
- Othman MHD, Ismail AF, Mustafa A, Malaysian Polym. J. (MPJ), 2, 10, 2007
- Shang XY, Fang SM, Meng YZ, J. Membr. Sci., 297(1-2), 90, 2007
- Jeong BY, Song SH, Baek KW, Cho IH, Hwang TS, Polym.(Korea), 30(6), 486, 2006
- Bebin P, Caravanier M, Galiano H, J. Membr. Sci., 278(1-2), 35, 2006
- Summer MJ, Harrison WL, Weyers RM, Kim YS, McGrath JE, Riffle JS, Brink A, Brink MH, J. Membr. Sci., 239(2), 199, 2004
참고문헌정보(참고문헌, 인용문헌)는 화학공학소재연구정보센터에 의해 제공되고 있습니다.