티타니움이 치환된 Silicalite(TS-1)의 제조 및 특성분석
Synthesis and Characterization of Titanium Silicalite-1(TS-1)
과산화수소를 이용한 탄화수소의 선택적인 산화반응에 유용한 촉매인 Titanium Silicalite-1(TS-1)의 제조와 특성분석에 관하여 XRD, FT-IR, Raman, TGA, SEM등을 이용하여 연주하였다. XRD를 이용하여 MFI구조의 생성을 확인하였으며, FT-IR은 MFI의 구조 생성과 아울러 그 격자내에 T가 치환되었음을 확인시켜 주었다. Ti의 양이 2.0 atomic %가 넘을 때는 부산물로서 anatase형의 TiO2가 생성됨을 Raman분광법으로써 확인하였다. 생성된 TS-1은 650℃까지는 열적으로 안정하여 0.25 μm정도의 균일한 입자크기를 가진 원통형 형상을 보였다. 합성과정 중 MFI구조는 170℃의 결정화 과정에서 형성되며 Ti가 silicalite격자내로 치환되는 시기는 550℃의 소성단계였다.
Synthesis and characterization of titanium silicalite-1(TS-1) have been studied by using XRD, FT-IR, Raman, TGA and SEM. The MFI structure of the prepared sample was confirmed by XRD and the results of FT-IR provided evidence of MFI structure and the substitution of Ti into silicalite lattice. When Ti content exceeded 2 atomic %, some Ti formed anatase TiO2 particles which was characterized by Raman spectroscopy. The product TS-1 was thermally stable up to 650℃ and formed cylinderical particles of uniform size of ca. 0.25 μm. The MFI structure was formed during crystallization step at 170℃ and Ti substitution into silicalite lattice occurred during calcination step at 550℃.
[References]
- Notari B, "Structure-Activity and Selectivity Relationships in Heterogeneous Catalysis," Elsevier, p. 243, 1991
- Notari B, Catal. Today, 18, 163, 1993
- Thangaraj A, Kumar R, Mirajkar SP, Ratnasamy P, J. Catal., 130, 1, 1991
- Astorino E, Peri JB, Willey RJ, Busca G, J. Catal., 157(2), 482, 1995
- Keshavaraja A, Ramaswamy V, Soni HS, Ramaswamy AV, Ratnasamy P, J. Catal., 157(2), 501, 1995
- Taramasso M, Perego G, Notari B, U.S. Patent, 4,410,501, 1983
- Duprey E, Beaunier P, Springuelhuet MA, Bozonverduraz E, Fraissard J, Manoli JM, Bregeault JM, J. Catal., 165(1), 22, 1997
- Rhee CH, Lee JS, Catal. Today, 38(2), 213, 1997
- Notari B, Adv. Catal., 41, 253, 1996
- Uguina MA, Serrano DP, Ovejero G, Vangrieken R, Camacho M, Appl. Catal. A: Gen., 124(2), 391, 1995
참고문헌정보(참고문헌, 인용문헌)는 화학공학소재연구정보센터에 의해 제공되고 있습니다.