In this study, the polyaniline films of emeraldine base(EB) and lucoemeraldine base(LEB) form chemically doping with poly(sodium-4 styrenesulfonate, PSS) were prepared by casting the mixed solution of chloroform and m-cresol on ITO(indium tin oxide) electrode. By analyzing UV-vis spectra of the mixed solutions, the effects of the secondary doping by m-cresol were obtained. And the conductivity of polyaniline film was increased with increasing m-cresol content. The results suggest that the improvement of conductivity obtained by secondary doping results primarily from interaction of polyaniline and m-cresol. As the results of analyzing cyclic voltammograms, it was known that the redox peak currents of polyaniline electrode prepared from LEB were larger and more reversible than those of polyaniline electrodes prepared from EB. The charge transfer resistances(Rct) of polyaniline electrodes were reduced with increasing m-cresol content, and LEB/PSS electrodes were smaller than EB/PSS electrodes. This result agrees to the analysis of the redox peak current of cyclic voltammograms. The solution resistance and the capacity of electrical double layer almost unchanged in all prepared polyaniline electrodes. It was confirmed that solution resistance was independent of frequency factor in AC impedance spectra. Also the polyaniline film doping with PSS was revealed pseudo n-type characteristics of conducting polymer.